<pre id="pbbj5"><nobr id="pbbj5"><big id="pbbj5"></big></nobr></pre>
<cite id="pbbj5"></cite>

<font id="pbbj5"><listing id="pbbj5"></listing></font><font id="pbbj5"><listing id="pbbj5"><output id="pbbj5"></output></listing></font>
      <sub id="pbbj5"></sub>

      <pre id="pbbj5"><output id="pbbj5"></output></pre>

      <delect id="pbbj5"><noframes id="pbbj5"><dl id="pbbj5"></dl>
      <delect id="pbbj5"><noframes id="pbbj5"><dl id="pbbj5"></dl>

            <var id="pbbj5"></var><delect id="pbbj5"><mark id="pbbj5"></mark></delect>
            <dl id="pbbj5"><menuitem id="pbbj5"><span id="pbbj5"></span></menuitem></dl>

            <pre id="pbbj5"><mark id="pbbj5"></mark></pre>

              <span id="pbbj5"></span>
                <del id="pbbj5"><progress id="pbbj5"><ol id="pbbj5"></ol></progress></del>

                  <address id="pbbj5"><nobr id="pbbj5"><menuitem id="pbbj5"></menuitem></nobr></address>

                        <pre id="pbbj5"><listing id="pbbj5"><big id="pbbj5"></big></listing></pre>

                        <sub id="pbbj5"></sub>

                          江西石墨模具的裂紋出現的原因

                          作者:jcshimo 發布時間:2022-04-01 09:29:13

                          江西石墨模具的裂紋出現的原因

                          石墨 是一種新型材料,因其具有良好的物理性和化學性,被廣泛的運用在各種各樣的行業中。例如:金屬冶煉鑄造、玻璃成型等,它的應用領域也在不斷擴大。那我們在使用石墨模具的過程中,為什么石墨模具會出現淬火裂紋呢

                            石墨模具出現淬火裂紋的主要原因如下:

                            1、螺紋孔、帶尖角、形狀復雜、厚薄不均等,使組織應力及熱應力過大。

                            2、熱處理后,電火花加工時,是硬化層中存在有顯微裂紋和比較高的拉伸應力。

                            3、存在有嚴重的網狀碳化物偏析。

                            4、熱處理操作不當(冷卻溫度過低、加熱或冷卻過快、冷卻時間過長、淬火冷卻介質選擇不當)。

                            5、淬火加熱溫度過高,從而引起過燒或者過熱的現象。

                            6、存在冷塑變形的應力或者機械加工。

                            7、返修淬火加熱時,沒有經過中間退火,再次進行加熱淬火。

                            8、熱處理的,磨削工藝不當。

                            9、石墨模具淬火之后回火保溫時間不足或者回火不及時。